Hwang, Chuen-Ming 2014-12-14T16:00:47Z 2014-12-14T16:00:47Z 10000-01-01 1981 1981 The transformation behavior of TiNiFe alloys of nominal composition Ti(,50)Ni(,47)Fe(,3) has been studied by transmission electron microscopy, electron diffraction, and electrical resistivity measurements in the temperature range between room temperature and liquid nitrogen temperature. Based Made available in DSpace on 2014-12-14T16:00:47Z (GMT). No. of bitstreams: 1 8203492.pdf: 5554091 bytes, checksum: 9a69baa3ddf223542bf6cbfadedfc037 (MD5) Previous issue date: 1981 Embargo set by: Seth Robbins for item 68833 Lift date: Forever Reason: Restricted to the U of I community idenfinitely during batch ingest of legacy ETDs Restricted to the U of I community idenfinitely during batch ingest of legacy ETDs U of I Only 201 p. Thesis (Ph.D.)--University of Illinois at Urbana-Champaign, 1981. http://hdl.handle.net/2142/68655 (UMI)AAI8203492 eng Engineering, Metallurgy Transformation Behavior of a Titanium(50)nickel(47)iron(3) Alloy text Metallurgy and Mining Engineering Metallurgical Engineering University of Illinois at Urbana-Champaign Dissertation Ph.D.