Ultrasonic wave reflection measurements on stiffening and setting of cement paste

Chung, Chul-Woo

Content Files
1_Chung_Chul-Woo.pdf

Permalink

https://hdl.handle.net/2142/15556

Description

Title
Ultrasonic wave reflection measurements on stiffening and setting of cement paste
Author(s)
Chung, Chul-Woo
Issue Date
2010-05-14T20:50:06Z
Director of Research (if dissertation) or Advisor (if thesis)
Popovics, John S.
Doctoral Committee Chair(s)
Popovics, John S.
Committee Member(s)
  • Struble, Leslie J.
  • Reis, Henrique M.
  • Mondal, Paramita
Department of Study
Civil & Environmental Eng
Discipline
Civil Engineering
Degree Granting Institution
University of Illinois at Urbana-Champaign
Degree Name
Ph.D.
Degree Level
Dissertation
Date of Ingest
2010-05-14T20:50:06Z
Keyword(s)
  • hydration
  • stiffening
  • setting
  • cement paste
  • ultrasonic wave reflection
  • premature stiffening
Abstract
The objective of this research is to extend the use of P-wave and S-wave ultrasonic wave reflection (UWR) to monitor stiffening and setting of portland cement paste. The research focuses especially on the very early hydration period, during the first hours after mixing. For such purpose, it is necessary to obtain higher measurement sensitivity, in this case by employing a buffer (high impact resistance polystyrene or HIPS) with acoustic impedance that is close to that of cement paste. The use of the HIPS buffer together with a new signal compensating method provide sensitive, accurate and reliable measurements on the stiffening and setting of early-age cement paste. In order to study the stability of the HIPS buffer, UWR responses from various chemical solutions are tested. The ability to characterize solution properties, such as solution concentration and density, with P-wave UWR is reported. UWR responses from dispersed and flocculated alumina suspensions are measured in order to provide deeper understanding of the UWR response from cement paste. P-wave UWR is affected by amount of segregation, and S-wave UWR is affected by extent of flocculation. Based on the findings of these fundamental experiments, P- and S-wave UWR responses from hydrating Portland cement paste are interpreted. Criteria to define set conditions based on UWR are proposed: initial set is defined as the time at which S-wave acoustic impedance of 0.09 MRayls occurs, and final set by the time at which minimum of the first time derivative of S-wave UWR curve occurs. S-wave UWR is also applied to characterize premature stiffening of cement paste, where premature stiffening is indicated by the rapid linear drop in S-wave UWR in the first hour after mixing. Finally, novel applications of P-wave UWR are proposed for cement paste, including sensing differences in paste w/c, resulting from changes in the solid content (density), and detection of the onset of partial debonding, most likely resulting from autogenous shrinkage of the paste.
Graduation Semester
2010-5
Permalink
http://hdl.handle.net/2142/15556
Copyright and License Information
Copyright 2010 Chul-Woo Chung

Owning Collections

Graduate Dissertations and Theses at Illinois PRIMARY
Graduate Theses and Dissertations at Illinois
Dissertations and Theses - Civil and Environmental Engineering